CHEMICAL |
Density |
Density |
Melting |
Boiling |
| METAL |
SYMBOL |
g/cm3 |
Lbs/in3 |
Point
o F |
Point
o F |
| Aluminum (Pure) |
Al |
2.70 |
0.0975 |
1220 |
3272 |
| Antimony |
Sb |
6.62 |
0.2391 |
1166 |
2516 |
| Arsenic |
As |
5.73 |
0.2070 |
1497* |
1139* |
| Bismuth |
Bi |
9.80 |
0.3541 |
520 |
2642 |
| Cadmium (Cast) |
Cd |
8.64 |
0.3125 |
610 |
1403 |
| Calcium |
Ca |
1.55 |
0.0560 |
1564 |
2522 |
| Copper (Cold Rolled) |
Cu |
8.94 |
0.3230 |
1981 |
4217 |
| Gold (Pure Cast) |
Au |
19.30 |
0.6973 |
1945 |
4712 |
| Iron (Pure) |
Fe |
7.90 |
0.2853 |
2795 |
5430 |
| Lead (Cast) |
Pb |
11.35 |
0.4091 |
621 |
2948 |
| Lead (Rolled) |
Pb |
11.37 |
0.4103 |
621 |
2948 |
| Magnesium |
Mg |
1.74 |
0.0628 |
1204 |
2007 |
| Nickel (Cast) |
Ni |
8.85 |
0.3200 |
2645 |
5252 |
| Silver (Pure) |
Ag |
10.50 |
0.3800 |
1761 |
3542 |
| Tellurium |
Te |
6.24 |
0.2240 |
846 |
2534 |
| Tin (Cast) |
Sn |
7.29 |
0.2633 |
450 |
4100 |
| Zinc (Cast) |
Zn |
7.14 |
0.2580 |
787 |
1661 |
|
|
* Under Pressure. Sublimes without melting at ordinary
pressure |
|
PHYSICAL
PROPERTIES OF LEAD |
| |
Atomic Number |
|
|
82 |
| |
Atomic Weight |
|
207.22 |
|
| |
Density |
20oC, Cast |
|
11.35 |
| |
|
327.4oC, Solid |
|
11.005 |
| |
|
327.4oC,
Liquid |
|
10.686 |
| |
|
550oC, Liquid |
|
10.418 |
| |
Atomic Volume |
|
|
18.27 |
| |
Melting Point oC |
|
|
327.4 |
| |
Boiling Point oC.,
at 760 mm Pressure |
|
1525-1620 |
| |
Specific Heat, per oC.,
cal per g |
|
0.030 |
| |
Latent Heat of fusion, cal per g |
|
5.47-6.26 |
| |
Coef. Of Linear expansion (17-100
oC) per
oC |
|
0.0000293 |
| |
Thermal conductivity, cal./cm2/oC/sec |
|
|
| |
|
at room temperature |
|
0.083 |
| |
Electrical resistivity, microhm/cm |
|
20.65 |
| |
Modulus of Elasticity in tension |
|
0.8-2.0 million |
| |
|
|
|
|
|
PHYSICAL
PROPERTIES OF TIN |
| |
Atomic Number |
|
|
50 |
| |
Atomic Weight |
|
118.7 |
|
| |
Density |
20oC, Cast |
|
7.29 |
| |
Atomic Volume |
|
|
16.23 |
| |
Melting Point oC |
|
|
232 |
| |
Boiling Point oC.,
at 760 mm Pressure |
|
2260 |
| |
Specific Heat, per oC.,
cal per g |
|
0.054 |
| |
Latent Heat of fusion, cal per g |
|
14.4 |
| |
Coef. Of Linear expansion (17-100
oC) per
oC |
|
0.000023 |
| |
Thermal conductivity, cal./cm2/oC/sec |
|
|
| |
|
at room temperature |
|
0.157 |
| |
Electrical resistivity, microhm/cm |
|
11.5 |
| |
Modulus of Elasticity in tension |
|
5.9-7.8 million |
| |
|
|
|
|
|
PHYSICAL
PROPERTIES OF
ANTIMONY |
| |
Atomic Number |
|
|
51 |
| |
Atomic Weight |
|
121.76 |
|
| |
Density |
20oC, Cast |
|
6.62 |
| |
Melting Point oC |
|
|
630 |
| |
Boiling Point oC.,
at 760 mm Pressure |
|
1380 |
| |
Coef. Of Linear expansion (17-100
oC) per
oC |
|
0.0000113 |
| |
Thermal conductivity, cal./cm2/oC/sec |
|
|
| |
|
at room temperature |
|
0.50 |
| |
Electrical resistivity, microhm/cm |
|
12.67 |
| |
|
|
|
|
|
PHYSICAL
PROPERTIES OF COPPER |
| |
Atomic Number |
|
|
29 |
| |
Atomic Weight |
|
63.57 |
|
| |
Density |
20oC, Cast |
|
8.94 |
| |
Melting Point oC |
|
|
1083 |
| |
Boiling Point oC.,
at 760 mm Pressure |
|
2325 |
| |
Specific Heat, per oC.,
cal per g |
|
0.0919 |
| |
Latent Heat of fusion, cal per g |
|
50.46 |
| |
Thermal conductivity, cal./cm2/oC/sec |
|
|
| |
|
at room temperature |
|
0.923 |
| |
Electrical resistivity, microhm/cm |
|
1.682 |
| |
|
|
|
|